What information can frictional properties of polymer brushes tell us?

We have used friction force microscopy (FFM) to quantitatively examine surface grown zwitterionic polymer brushes: poly(2-(methacryloyloxy)ethyl phosphorylcholine) (PMPC), and to establish the correlation between its frictional behaviour to other intrinsic properties. In a good solvent, it was found that the coefficient of friction ($\mu$) decreased with increasing film thickness. We conclude that the amount of bound solvent increases as the brush length increases, causing the osmotic pressure to increase and yielding a reduced tendency for the brush layer to deform under applied load. When measured in a series of alcohol/water mixtures, a significant increase in $\mu $ was observed for ethanol/water mixtures at a volume fraction of 90{\%}. This is attributed to brush collapse due to co-nonsolvency, leading to loss of hydration of the brush chains and hence substantially reduced lubrication. We show that single asperity contact mechanics is strongly dependent on solvent quality. Friction-load relationship was found linear in methanol (good solvent), but sub-linear in water and ethanol (moderate solvent).