Nanoconfined Ferroelectricity in Polymers*

In this presentation, a low loss polystyrene (PS) was grafted as side chains onto the P(VDF-CTFE) main chain. After PVDF crystallization, dielectric PS side chains were segregated to the crystalline-amorphous interface, forming a finite confinement layer for ferroelectric PVDF crystals. We speculated that less space charge was induced during electric poling because of the nanoscale confinement effect. Consequently, a fast discharge speed, relatively high energy density, and low losses were achieved.